Ionic groups incorporated into a polymer have a decided effect on its physical properties. A number of ionomers and polyelectrolytes have been widely applied. In particular, sulfonated bisphenol-A polysulfone (SPSF) has been used as a composite or single-component membrane for the desalination of water. In this article, the synthesis and physical characteristics of sulfonated polysulfone are addressed. A detailed synthesis route is provided and methods that yield determinable levels of sulfonation are described. These ion-containing polymers retain an excessive amount of residual salts, which, of course, are impurities to the system. Therefore, before any analyses were made the polymers were subjected to a thorough soxhlet extraction process with boiling water, which appeared to be quite effective. The degree of sulfonation was assessed by several methods such as 1H NMR and FT-IR. A new 1H NMR method was derived because the method cited in the literature proved to be too inconsistent for our work. The new 1H NMR method used a quaternary ammonium counterion [N(CH3)4]. These methyl protons are easily measured and may be ratioed against the isopropylidene protons in the polymer backbone that act as an internal standard. Characterization of the physical properties of SPSF consisted of water uptake, differential scanning calorimetry (DSC), thermomechanical analysis (TMA), and solubility studies. Its physical appearance and mechanical behavior were improved by the solution procedure. Also addressed were the effects of different counterions (Na+ & Mg++) with SPSFs of low levels of sulfonation. The variation in physical properties between the divalent and monovalent counterions is dramatic, especially when observed by TMA in the rubber plateau above the apparent glass temperature.
Zusätzliches Material:
12 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/pol.1984.170220320
Permalink