Abstract Single crystals of the nominal composition Bi2V0.9Ni0.1O5.35 were prepared. They were studied by TGA/DTA, impedance spectroscopy and electron diffraction. The impedance of the crystals with Pt electrodes was measured in two directions: parallel and perpendicular to the layers of the intergrowth structure in the frequency range 10−2−107 Hz at temperatures between 300 and 940 K. Arrhenius type plots for both directions show two linear regions with different activation energies. In the low temperature region the conductivity in the direction parallel to the layers was by a factor of about 1000 larger than in the perpendicular direction. In the high temperature region the ratio of conductivities was about 100. A time dependence of the conductivity in the perpendicular direction was observed during heating and cooling in limited temperature ranges. The electron diffraction experiments gave evidence that the superlattice spots present in the diffraction patterns at low temperature, disappear reversibly at temperatures higher than 650 K. The transition temperatures observed in the DTA and in the electron diffraction experiments correspond to the temperature of changes of the activation energy. An order-disorder transition of oxygen ions is considered to be responsible for this phenomenon.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF02375900
Permalink