ISSN:
0044-2313
Keywords:
Calciumcarbide Chloride
;
Synthesis
;
Crystal Structure
;
Allylenide Ion
;
Chemistry
;
Inorganic Chemistry
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Chemistry and Pharmacology
Description / Table of Contents:
Synthesis and Crystal Structure of a Calciumcarbide Chloride Containing a C34- Unit, Ca3Cl2C3Ca3Cl2C3 was prepared from calcium, CaCl2 and graphite in sealed tantalum capsules. Red, transparent crystals were obtained from heating the mixture to 900°C (for one day) and annealing afterwards at 780°C for three days. The compound forms a layered structure (Cmcm, Z = 4, a = 384.24(9) pm, b = 1340.7(3) pm, c = 1152.6(3) pm, R = RW = 0.036 for 481 independent intensities) with alternating stacks of double layers of Ca2+ and monolayers of Cl-. The double layers of calcium contain allylenide ions, C34-. The latter exhibit C2v symmetry, a bond angle (C—C—C) of 169.0(6)° and a C—C separation of 134.6(4) pm.
Notes:
Ca3Cl2C3 entsteht aus Calcium, CaCl2 und Graphit in verschweißten Tantal-Kapseln in Form roter, transparenter Kristalle durch Erhitzen des Reaktionsgemenges auf 900°C (1 Tag) und anschließendes dreitägiges Tempern bei 780°C. Die Verbindung kristallisiert in einer Schichtstruktur (Cmcm, Z = 4, a = 384,24(9) pm, b = 1 340,7(3) pm, c = 1 152,6(3) pm, R = RW = 0,036 für 481 unabhängige Intensitäten) mit einer alternierenden Anordnung von Doppelschichten aus Ca2+ und Schichten aus Cl-. In den Calcium-Doppelschichten liegen die Allylenidionen, C34-. Sie zeigen C2v-Symmetrie mit einem Bindungswinkel (C—C—C) von 169,0(6)° und dem C—C-Bindungsabstand von 134,6(4) pm.
Additional Material:
2 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19915930118
Permalink