ISSN:
1435-1536
Keywords:
Elastizitätsmodul
;
Polyäthylen
;
Biegeschwingungen
Source:
Springer Online Journal Archives 1860-2000
Topics:
Chemistry and Pharmacology
,
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Description / Table of Contents:
Abstract An apparatus is described which causes forced bending vibrations of cylindrical polymer samples in the frequency range of 1 to 10 Hz. Samples are clamped at one end; the other end is vibrating with constant amplitude, and bending forces are registered. By variation of the bending length of samples Young's modulus E0 at zero deformation can be calculated by means of an extrapolation method. To determine the true bending length of samples an additional constant lengthΔL is introduced. Measurements of high density polyethylene at 22 °C yieldE 0=2430 N/mm2 at 1 Hz. The results are compared with those of resonant vibrations.
Notes:
Zusammenfassung Es wird eine Apparatur zur erzwungenen Wechselbiegung zylindrischer Polymerproben im Frequenzbereich von 1 bis 10 Hz beschrieben. Ein Probenende wird fest eingespannt, das andere um einen konstanten Betrag ausgelenkt und die Biegekraft dabei gemessen. Durch Variation der Biegelänge der Proben kann man nach einem einfachen Extrapolationsverfahren den ElastizitätsmodulE 0 bei der Deformationε=0 bestimmen. Dabei wird die Einführung einer konstanten ZusatzlängeΔL zur Ermittlung der wahren Biegelänge begründet. Messungen an Polyäthylen hoher Dichte bei 22 °C ergabenE 0=2430 N/mm2 bei 1 Hz. Die Übereinstimmung mit den Ergebnissen von Resonanzmethoden wird diskutiert.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01422589
Permalink