ISSN:
1042-7147
Schlagwort(e):
epoxy resin
;
phosphorylated hardener
;
combusion
;
fire retardancy
;
Chemistry
;
Polymer and Materials Science
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
,
Maschinenbau
Notizen:
The kinetics of curing tetraglycidyl 4,4′-diaminodiphenyl methane (TGDDM) or of the mixture TGDDM/diglycidylether of bisphenol A (DGEBA) by bis(m-aminophenyl)methylphosphine oxide (BAMPO) was studied using differential scanning calorimetry. At low advancement of curing (〈50%), the low activation energy interaction between epoxy and amino groups seems to be controlled by diffusion, whereas above 50% the role of homopolymerization tends to increase and the process becomes chemically controlled.BAMPO shows a higher fire-retardant effectiveness in the mixture TGDDM/DGEBA than in TGDDM or DGEBA alone, for which the oxygen and nitrous oxide index tests suggest a condensed phase or a gas phase fire-retardant action depending on phosphorus content. An intumescent char is formed on the surface of burning fire-retarded specimens which tends, however, to be oxidized, thus reducing the fire-proofing effect at high BAMPO content.
Zusätzliches Material:
10 Ill.
Materialart:
Digitale Medien
Permalink