Y-Ba-Cu-O
;
oxycarbonate
;
sol-gel
Source:
Springer Online Journal Archives 1860-2000
Topics:
Chemistry and Pharmacology
Notes:
Abstract High T c -superconducting powders of the Y-Ba-Cu-O system are prepared by a solution-polyacrylamide gel using citric acid as a complexing agent. This method provides an easy way to prepare reactive YBaCuO powders by sol-gel synthesis. However this synthesis involves intermediate phases formation which impedes the obtention of the pure phase at low temperature. An intermediate oxycarbonate phase forms between 800° and 850°C in flowing oxygen. From powder X-ray diffraction, thermal analysis and IR spectroscopy, it is concluded that the intermediate oxycarbonate has an average tetragonal structure—SG P4/mmm—similar to that of the parent oxide with a stoichiometry close to YBa2Cu2.95(CO3)0.35O6.6. The carbonate group is located in the center of the basal CuO square. This compound has superconducting properties. A pure 123 phase is obtained when the xerogel precursor is annealed at 925°C in O2 or at 800°C in Ar, then in O2. The grain growth and microstructure development of YBaCuO have also been investigated and compared using two different powders, i.e. sol-gel route and commercial powder from Hoechst.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00486284
Permalink