Abstract The evolution of the nature and concentration of the defects produced by 100 or 300 keV As ions at fluences 1 to 4×10−12 cm−2 inn-type, Fz Silicon doped with 1015 to 1016 cm−3 has been studied as function of thermal treatments (in the range 500°–900 °C) and of the energy density (in the range 0.3–0.6 J cm−2) of a light pulse from a ruby laser (15 ns, 0.69 μm). Deep-level transient spectroscopy (DLTS) combined with capacitance — voltage (C-V) measurements were used to get the characteristics (energy level, crosssection for the capture of majority carriers) of the defects and theirs profiles. The difficulties encountered in the analysis of the results, due to the large compensation of free carriers in the implanted region and to the abrupt defect and free carrier profiles, are discussed in detail and the corrections to apply on the C-V characteristics and the DLTS spectra are described. The defects resulting from the two types of treatments are found to be essentially the same. Only, for laser energies higher than ∼0.5 J cm−2, the laser treatment appears to introduced new defects (atE≧0.32 eV) which should result from a quenching process. The fact that a laser energy smaller than the threshold energy for melting and recrystallization is able to anneal, at least partially, the defects produced by the implantation, demonstrates that the annealing process induced by the laser pulse is not a purely thermal process but is enhanced by a mechanism involving ionization.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00617567
Permalink