Description / Table of Contents:
The reaction of α,ω-dihalogeno-alkanes with sodium and a consecutive catalytic hydrogenation results in a mixture of paraffins with a discontinuous distribution of molecular weight. Starting with 1.10-dibromodecane only paraffins with 10, 20, 30 etc. carbon atoms are obtained, whereas 1.20-dibromoeicosane produces a mixture of paraffins with 20, 40, 60 etc. carbon atoms. These mixtures of paraffins were separated by gel chromatography into monodisperse compounds. The highest molecular paraffine thus obtained was C140H282.With C70H142 as an example the temperature dependence of the small angle X-ray diffraction has been measured. From the intensity and position of the long period reflexion the variation of three structure parameters could be ascertained, suited for the characterization of the lamellar structure.
Notes:
Die Umsetzung von α,ω-Dihalogenalkanen mit Natrium führt nach anschließender katalytischer Hydrierung zu einem Paraffingemisch mit diskontinuierlicher Molekulargewichtsverteilung. So enthält das aus 1.10-Dibromdecan hergestellte Produkt nur Paraffine mit 10, 20, 30 usw. C-Atomen, ein aus 1.20-Dibromeicosan hergestelltes Produkt dagegen nur die Paraffine mit 20, 40, 60 usw. C-Atomen. Diese Paraffingemische wurden gelchromatographisch in die molekulareinheitlichen Verbindungen zerlegt und Paraffine bis C140H282 isoliert.Am Beispiel des C70H142 wurde die Temperaturabhängigkeit der Röntgenkleinwinkelstreuung gemessen. Aus Intensität und Lage der Langperiodenreflexe ließen sich die Änderungen von drei Strukturparametern ermitteln, die zur Charakterisierung der Lamellarstruktur geeignet sind.
Additional Material:
9 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/macp.1972.021620107
Permalink