Pitting and contact corrosion in magnesium-canned fuel rodsWhen nuclear fuel elements - containing Mg, graphite and Zircaloy - are stored in water there is the danger of contact corrosion of Mg in contact wit graphite; in partcular when cholorides are present (even in traces) there exists the danger of pitting corrosion. Only at pH values 〉 11,5 a bydroxide layer is formed which yields a certain protection. The pitting potential in alkaline waters is shifted to more negative values with incrasing chloride contents; this displacement can be prevented by inhiitors. Most efficient is the addition of sodium carbonate which gives rise to the formation of a protective hydromagnesite layer.
Notizen:
Bei Lagerung verbrauchter Brennstoffelemente - Werkstoffe Mg, Graphit, Zircaloy - in Wasser besteht die Gefahr der Kontaktkorrosion von Mg bei Kontakt mit Graphit; besonders bei Anwesenheit von Chloriden besteht Lochfraßgefahr. Erst bei pH Werten 〉 11,5 entsteht eine Hydroxidschicht, die einen gewissen Schutz bewirkt. Das Lochfraßpotential im alkalischen Wasser verschiebt sich mit zunehmendem Chloridgebalt stark in den Bereich negativer Werte, was durch Inhibitoren verhindert werden kann. Am günstigsten ist Zusatz von Natriumcarbonat, das zur Bildung eines Schutzfilms aus Hydromagnesit führt.
Zusätzliches Material:
12 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/maco.19680191010
Permalink