Summary The stress relaxation of the polycarbonate of bisphenol-A was systematically studied as a function of the degree of crystallinity (from zero to 18%). The time-temperature equivalence principle was found applicable and for each degree of crystallinity a separate master curve could be constructed. The amount of crystalline material modifies gradually the shape of the master curve. The glass transition region is broadened and the flow region eliminated above 9% crystallinity. The experimental values of the shift factor fit a unic W.L.F. equation. The characteristic reference temperatureT i rises progressively with the degree of crystallinity.
Notes:
Résumé On a étudié par la méthode de la relaxation de la contrainte la variation du comportement viscoélastique du polycarbonate de bisphénol-A de cristallinité variable entre zéro et 18%. On a pu appliquer le principe d'équivalence des effets du temps et de la température et construire pour chaque taux de cristallinité une courbe pilote. La cristallisation entraîne une modification progressive de la forme de la courbe pilote. La région de transition vitreuse s'élargit à mesure que le taux de cristallinité s'élève. A partir d'un taux de cristallinité de 9% la région d'écoulement est totalement supprimée. On constate aussi que les valeurs expérimentales du facteur de temps obéissent à l'équation de W.L.F. et que la température caractéristiqueT i s'élève légèrement avec le taux de cristallinité.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01976237
Permalink