ISSN:
1573-2711
Keywords:
Al-Si alloy
;
antiwear
;
ZDDP
;
X-ray absorption
;
P L-edge XANES
Source:
Springer Online Journal Archives 1860-2000
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract The boundary lubrication of Al alloys 6061 (Al-6% Si) and A-390 (Al-18 wt% Si), by a sec-ZDDP (zinc dialkyldithiophosphate) oil blend was examined at 60 and 100°C. The wear performance in the ZDDP blend was an improvement on base stock. At 100°C the ZDDP prevented scuffing, though no antiwear films could be detected due to the severe wear. At 60°C all samples showed initial scuffing followed by a more controlled wear given by an embedded antiwear film. P L-edge X-ray near-edge structure (XANES) spectroscopy using synchroton radiation was used to characterize the antiwear and thermally generated deposition films on the Al alloys. P L-edge XANES results of the antiwear films at 100°C showed the absence of a polyphosphate film. A well-developed polyphosphate film was indicated at 60°C, very similar to that formed on steel at 100°C. P L-edge XANES results of the thermal deposition films showed the presence of only unchanged sec-ZDDP at 125°C with no polyphosphate present. A polyphosphate film was present at 200°C, similar to the antiwear film for Al alloy at 60°C and steel at 100°C.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF00174260
Permalink