Fatigue & fracture of engineering materials & structures
26 (2003), S. 0
ISSN:
1460-2695
Quelle:
Blackwell Publishing Journal Backfiles 1879-2005
Thema:
Maschinenbau
Notizen:
The fatigue crack growth behaviour of 0.47% carbon steel was studied under mode II and III loadings. Mode II fatigue crack growth tests were carried out using specially designed double cantilever (DC) type specimens in order to measure the mode II threshold stress intensity factor range, ΔKIIth. The relationship ΔKIIth 〉 ΔKIth caused crack branching from mode II to I after a crack reached the mode II threshold. Torsion fatigue tests on circumferentially cracked specimens were carried out to study the mechanisms of both mode III crack growth and of the formation of the factory-roof crack surface morphology. A change in microstructure occurred at a crack tip during crack growth in both mode II and mode III shear cracks. It is presumed that the crack growth mechanisms in mode II and in mode III are essentially the same. Detailed fractographic investigation showed that factory-roofs were formed by crack branching into mode I. Crack branching started from small semi-elliptical cracks nucleated by shear at the tip of the original circumferential crack.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1046/j.1460-2695.2003.00644.x
Permalink
| Bibliothek |
Standort |
Signatur |
Band/Heft/Jahr |
Verfügbarkeit |