preoxidation
;
coal gasification
;
alumina-former
;
mechanical alloy
Quelle:
Springer Online Journal Archives 1860-2000
Thema:
Maschinenbau
Notizen:
Abstract Iron-based mechanical alloys containing 3.2–6.6 Al, 16.0–24.7 Cr, 0.5 Ti, and 0.5 Y2O3 (mass%) were preoxidized in air at 1373 K for 10–180 min. Alumina scales were formed. Scales were isolated and examined in a high-voltage transmission electron microscope. Specimen sections were examined in a scanning electron microscope. Specimens were exposed to atmospheres exhibiting oxygen activities from 1.5×10−13 to 1.4×10−14 and sulfur activities from 7.4×10−7 to 3.6×10−5 at 1123, 1223, and 1323 K. Alumina, chromia, and iron sulfide are thermodynamically stable under these conditions. Sulfidation did not occur at 1223 or 1323 K. Specimens exposed at 1123 K were sulfidized and formed a scale containing iron, chromium, and sulfur. The period before the onset of sulfidation was dependent on the preoxidation time. A model is developed to account for the temperature dependence of the sulfidation in terms of the alloy-interdiffusion rate of aluminum and the activity of the sulfidizing species at the scale-gas interface.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1007/BF00665266
Permalink