Description / Table of Contents:
Properties of electrolyte films formed through atmospheric corrosionAn investigation has been carried out into the composition of the electrolyte films which are formed on non-metallic materials (glass) as well as on metals (Cu, Zn, Fe) in an atmosphere containing SO2. Fresh as well as pre-corroded specimen were used. It was found that the SO2 absorbed in the solution is very rapidly oxidized into SO42- if the electrolyte film contains dissolved particles of the corrosion products. With 1 to 55 ppm SO2 in the atmosphere, the change in the pH value of the electrolyte is but small and does not vary with the SO2 partial pressure.
Notes:
Die Zusammensetzung der auf nichtmetallischen Materialien (Glas) sowie auf Metallen (Cu, Zn, Fe) an SO2-haltiger Atmosphäre entstehenden Elektrolytfilme wurde untersucht, wobei sowohl frische als auch vorkorrodierte Proben verwendet wurden. Dabei stellte sich heraus, daß das in der Lösung aufgenommene SO2 sehr rasch zu SO42- oxydiert wird, wenn der Elektrolytfilm gelöste Anteile aus den Korrosionsprodukten enthält. Der pH-Wert des Elektrolyten ändert sich bei 1 bis 55 ppm SO2 in der Atmosphäre nur wenig und nicht entsprechend dem SO2-Partialdruck.
Additional Material:
3 Tab.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19700210104
Permalink