Cellulose benzoates with degrees of substitution between 2.8 and 2.9 were synthesized in a one-step reaction of cellulose with benzoyl chloride in presence of pyridine as base. Their molecular weights were in the range 140000-100000; the glass transition temperature and the melting temperature were 155 and 274°C, respectively. The esters are readily soluble in organic solvents such as N,N-dimethyl formamide, chloroform and dichloromethane and show good thermal resistance up to 250°C. Because of the brittle character of cellulose benzoate, plasticizer (diethyl phthalate) must be added for the fabrication of films and workable, moulded parts. As shown by stress-strain and impact measurements, the hard and brittle character is retained for plasticizer contents up to 20 wt.-%.
Notes:
Cellulosebenzoate mit Substitutionsgraden von 2,8-2,9 wurden in einer einstufigen Reaktion durch Umsetzung von Cellulose mit Benzoylchlorid in Gegenwart von Pyridin als Base hergestellt. Die Molekulargewichte der Cellulosebenzoate lagen zwischen 140000 und 100000; die mittels DSC gemessene Glastemperatur Tg betrug 155°C, die Schmelztemperatur TS 274°C. Die Ester sind gut löslich in organischen Lösungsmitteln wie N,N-Dimethylformamid, Chloroform und Dichlormethan und besitzen ferner eine gute thermische Beständigkeit bis ca. 250°C. Filme und nacharbeitbare Preßlinge aus Cellulosebenzoat lassen sich aufgrund der hohen Sprödigkeit nur durch Zumischen eines Weichmachers (Diethylphthalat) herstellen. Dabei bleibt das hart-spröde Verhalten, wie Zug-Dehnungs-Versuche und Schlagzähigkeitsmessungen zeigten, bis zu einem Weichmacheranteil von 20 Gew.-% bestehen.
Additional Material:
2 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1994.052200117
Permalink