Investigations on the Effect of Microstructure on Crack Propagation during Unidirectional Loading of TiAl6V4Fracture mechanics tests were performed with the titanium alloy Ti-6 Al-4 V between -196°C and room temperatur. Crack propagation behaviour was characterized by the K-Δa-curve, KIo at the onset of stable crack extension and by KQ, determined with the 5% secant method. KQ is strongly dependent on the microstructure, whereas there is a less effect on KIo. For a material with a microstructure with a low fracture toughness the value KQ can be increased considerably by vaccum annealing at 750°C. There is only a small decrease of the yield strength.
Notes:
An der Titanlegierung TiAl6V4 wurden Bruchmechanikversuche zwischen -196°C und Raumtemperatur durchgeführt. Die Charakterisierung des Rißausbreitungsverhaltens erfolgte durch die K-Δa-Kurve bzw. durch KIobeim Einsetzen der stabilen Rißverlängerung und KQ, bestimmt mit dem 5% Sekantenverfahren. Die Gefügeausbildung hat einen großen Einfluß auf KQ, der Einfluß auf KIo ist geringer. Bei einem Material mit Gefüge mit niedriger Rißzähigkeit kann KQ durch eine Glühbehandlung bei 750°C im Vakuum beträchtlich erhöht werden. Die Streckgrenze sinkt dabei nur unwesentlich ab.
Additional Material:
14 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/mawe.19780090404
Permalink