Diffusion in the contact zone of explosion-welded titanium-clad steel plates. After diffusion heat treatment, the intermetallic compounds Fe2Ti and FeTi were found to exist in the contact zone of titanium - Clad steel plates. The bond strength of these clad plates may possibly be impaired by the segregation of titanium carbide in the FeTi layer. In addition, cavities form adjacent to the intermetallic phases in the titanium after prolonged heat treatment. Titanium concentration in the fusion zones was found to be 55 ± 2 w/o (balance iron). After heat treatment of this specimen, FeTi was found to be predominant.
Notes:
Nach Diffusionsglühungen konnten in der Kontaktzone von Fe/Ti-Plattierungen die intermetallischen Verbindungen Fe2Ti und FeTi nachgewiesen werden. Die Haftfestigkeit dieser Plattierungen kann möglicherweise durch Ausscheidung von Titan-Karbid in der FeTi-Zone beeinträchtigt werden. Bei längerer Glühzeit bilden sich zusätzlich Löcher neben den intermetallischen Phasen im Titan aus. Die Titan-Konzentration in den Aufschmelzzonen konnte mit 55 ± 2 Gew.-% Titan (Rest Eisen) bestimmt werden. Nach einer Wärmebehandlung dieser Probe wurde überwiegend FeTi nachgewiesen.
Additional Material:
10 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/mawe.19720030103
Permalink