BaAg2S2, a Thioargentate with the CaAl2Si2-Type StructureBaAg2S2 could be obtained as crystalline powder by the reaction of barium-bis[dicyanoargentate(I)] in a stream of hydrogensulfid at 500°C. Single crystals grew at 480°C in an evacuated glass ampoule filled with a flux of potassium thiocyanate and powdery BaAg2S2 as solid. BaAg2S2 crystallises in the trigonal CaAl2Si2-typ structure, a = 4.386(1) Å, c = 7.194(2) Å, space group P3m1, Z = 1. The structure was determined from four-circle diffractometer data. The silver-sulphur distances are discussed with respect to the corresponding distances of the hitherto known alkaline earth-transition metal pnictides, also crystallizing in the CaAl2Si2-typ structure.
Notes:
BaAg2S2 wurde als kristallines Pulver bei der Umsetzung von Barium-bis[dicyanoargentat(I)] im Schwefelwasserstoffstrom bei 500°C erhalten. Einkristalle entstanden in einer evakuierten Glasampulle, in der das pulverförmige BaAg2S2 mit Kaliumrhodanid als Flußmittel bei 480°C erhitzt wurde. BaAg2S2 kristallisiert trigonal im CaAl2Si2-Typ, a = 4,386(1) Å, c = 7,194(2) Å, Raumgruppe P3m1, Z = 1. Die Struktur wurde mit Einkristalldiffraktometerdaten verfeinert. Die Silber-Schwefel-Abstände werden vergleichend mit den entsprechenden Abständen der bisher bekannten und ebenfalls im CaAl2Si2-Typ kristallisierenden Erdalkaliübergangsmetallpniktide diskutiert.
Additional Material:
1 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19976230906
Permalink