A feasibility study was conducted, in order to fabricate WC-Co powder granule ashigh-performance feedstock for thermal spraying process, by spray drying weakly flocculated nano-particulate slurries under various conditions. The defects were evaluated with respect to the amount of additives to prepare spherical WC-Co feedstock powders with few morphological defects and homogeneous microstructures. The characteristics of feedstock powders heat-treated at 850~ 1200ı were analyzed using SEM, EPMA, and Hg-porosimetry. The microstructure investigation revealed that the relative portion of larger pores around 10 µm increased with increasing heattreatment temperature. On the other hand, the relative portion of smaller pores of 1 µm decreased due to the coalescence of WC particles, leading to dense feedstock powders with less defects such as hollow or craters. The hardness of thermal-sprayed coat developed with the feedstock in this study, which had exceptionally high feedstock strength, was superior to that of any other sprayed coat obtained with commercial feedstock powders
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/09/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.475-479.2891.pdf
Permalink