Electronic Resource
Woodbury, NY
:
American Institute of Physics (AIP)
Applied Physics Letters
64 (1994), S. 61-63
ISSN:
1077-3118
Source:
AIP Digital Archive
Topics:
Physics
Notes:
Epitaxial V0.6Nb0.4N/NbN superlattices have been deposited on MgO(100) by reactive magnetron sputtering. The V0.6Nb0.4N alloy was chosen for one layer, rather than VN, in order to reduce the lattice mismatch from 5.7% to 3.5%, allowing growth of superlattices with relatively planar layers. The elastic moduli of NbN and V0.6Nb0.4N are nearly equal, in contrast to previously studied high-hardness nitride superlattices where the layer moduli differed substantially. Vickers microhardness measurements showed no measurable deviation (〈4 GPa) from alloy values. The results verify that the difference in layer elastic moduli is the primary parameter determining nitride superlattice hardening.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1063/1.110922
Permalink
Library |
Location |
Call Number |
Volume/Issue/Year |
Availability |