    Technological features of VNS-2 and ÉP817 maraging steels (1984)
    Springer
    Metal science and heat treatment 26 (1984), S. 66-70 
    Details
    ISSN: 1573-8973
    Quelle: Springer Online Journal Archives 1860-2000
    Thema: Maschinenbau
    Notizen: Conclusions 1. To maintain the high design strength of VNS-2 and ÉP817 steels it is necessary to provide stability in their properties and gas absorption and also a uniform original structure, i. e., to accomplish the production operations on them with the minimum possible change in properties, using, in particular, heating for deformation and hardening in inert media and welding with the minimum power per length (electron beam or laser). 2. In the design of parts and assemblies made of maraging steels and the development of production operations for their production it is necessary to include the possibility of a homogenizing heat treatment of weld joints (annealing, hardening, and aging).
    Materialart: Digitale Medien
    URL: http://dx.doi.org/10.1007/BF00712868
    Bibliothek Standort Signatur Band/Heft/Jahr Verfügbarkeit
    BibTip Andere fanden auch interessant ...
    Artikel (Nationallizenzen)
    Volltext
  • 2
    Digitale Medien
    Digitale Medien
    Properties of maraging steels VNS-2 and ÉP817 after aging (1983)
    Springer
    Metal science and heat treatment 25 (1983), S. 304-308 
    Details
    ISSN: 1573-8973
    Quelle: Springer Online Journal Archives 1860-2000
    Thema: Maschinenbau
    Notizen: Conclusions 1. Steel ÉP817 quenched from 1000° (1 h)+cold treatment at−70° for 2 h+aging at 510° for 3 h has a better combination of physical and mechanical properties than steel VNS-2 quenched from 1000° (1 h) and aged at 410–450° for 3 h. 2. Heating in the range of 400–450° induces, along with aging, destabilization of retained austenite, which is accompanied by local stresses. This has a substantial effect on the technological and operational reliability of the steel.
    Materialart: Digitale Medien
    URL: http://dx.doi.org/10.1007/BF00778329
    Bibliothek Standort Signatur Band/Heft/Jahr Verfügbarkeit
    BibTip Andere fanden auch interessant ...
    Artikel (Nationallizenzen)
    Volltext
Schließen ⊗
Diese Webseite nutzt Cookies und das Analyse-Tool Matomo. Weitere Informationen finden Sie hier...