Fatigue Crack Growth in a 13% Chromium Steel at Frequencies from 10-3 to 104 Hertz. Determination of the Threshold Stress Intensity ΔK0 by Ultrasonic FatigueFracture mechanics fatigue crack growth tests were run with loading frequencies from 10-3 to 104 Hertz. The results show that the environmental effects on fatigue crack growth decrease strongly at higher frequencies. Ultrasonic fatigue tests in water yield the same crack growth rates as low frequency fatigue tests in vacuum. Ultrasonic fatigue tests allow the measurement of the fatigue threshold stress intensity ΔK0 within reasonable testing times.
Notes:
Bruchmechanische Ermüdungsversuche wurden sowohl niederfrequent (bis 10-3 Hertz) als auch hochfrequent (mit Hilfe von Ultraschall und Hochgeschwindigkeitschromatographie bis 2,1 × 104 Hertz) durchgeführt. Dabei zeigt sich, daß der Einfluß korrosiver Umgebungen auf die Ermüdungsrißwachstumsgeschwindigkeit zu höheren Frequenzene hin abnimmt. Ultraschallermüdung des Stahls in Wasser führt zu gleichen Rißgeschwindigkeiten wie niederfrequente Ermüdung im Vakuum. Insbesondere für den Bereich kleiner Spannungsintensitätswerte bietet der Ultraschall-Ermüdungsversuch den Vorteil, den Schwellwert ΔK0 der Spannungsintensität, unter dem kein Rißfortschritt festzustellen ist, in kurzer Zeit zu ermitteln.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/mawe.19800110905
Permalink