Abstract A 16-spark gap, modified schardin-type camera was constructed for use in dynamic photoelastic analysis of fracturing plastic plates. Using this camera system, dynamic photoelastic patterns in fracturing Homalite-100 plates, 3/8 in. × 10 in. × 15 in. with an effective test area of 10 in. × 10 in., loaded under fixed grip condition were recorded. The loading conditions were adjusted such that crack acceleration, branching, constant velocity, deceleration and arrest were achieved. The Homalite-100 material was calibrated for static and dynamic properties of modulus of elasticity, Poisson's ratio, and stress-optical coefficient. For dynamic calibration, a Hopkinson bar setup was used to record the material response under constant-strain-rate loading conditions. The precise location of the dynamic isochromatic patterns in relation to the crack tip was determined by a scanning microdensitometer. This information was then used to determine dynamic stress-intensity factors which were compared with corresponding static stress-intensity factors determined by the numerical method of direct stiffness. Although the response of the dynamic stress-intensity factor to increasing crack length was similar to the static stress-intensity-factor response, the dynamic values were approximately 40 percent higher than the static values for constant-velocity cracks. for decelerating cracks, the peak values of dynamic stress-intensity factors were 40 percent higher than the corresponding static values.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF02325114
Permalink