Investigations on the Tribochemical Hydrolysis of 2H—TaS2 and on the Thermal Decomposition of Partially Hydrolysed 2H—TaS2On intense grinding of 2 H-TaS2 in automatic mortars a partial hydrolysis occurs, accompanied by evaluation of H2S. Also traces of atmospheric water are intercalated. It is shown that texture-effects in powder diagrams are reduced significantly by grinding. The critical temperature indicating superconductivity is raised from 0.7 K to 1.8 K by the grinding procedure.The thermal decomposition of ground TaS2 starts at 185° C and a maximum is reached at 233° C. The gaseous decomposition products are monitored by DTA-TG-QMS technique and consist of H2O, H2S, SO2 and simple sulfur fragments S, S2, and S3. Up to 1000° C a total mass-loss of 18.5% is monitored and solid decomposition products are TaS2-x and Ta2S.
Notes:
2H—TaS2 unterliegt beim Kugelmahlprozeß in der Schwingmühle einer partiellen Hydrolyse unter H2S-Freisetzung; außerdem werden Spuren von Wasser aus der Atmosphäre eingelagert. Das gemahlene TaS2 zeigt im Pulverdiffraktogramm nur geringe Textureffekte, die Sprungtemperatur, die den Übergang in den supraleitenden Zustand markiert, steigt von 0,7 K für nicht vorbehandeltes Disulfid auf 1,8 K an.Das gemahlene TaS2 ist thermolabil-der thermische Abbau wurde mit DTA—TG—QMS Technik untersucht. Die Zersetzung beginnt bei 185°C und erreicht ein Maximum bei 233°C durch Abspaltung von H2O, H2S, SO2 und den Schwefelfragmenten S, S2, und S3. Im Temperaturbereich von RT bis 1000°C wird ein maximaler Massenverlust von 18,5 Gew.% registriert, als Abbauprodukte können TaS2-x und das Subsulfid Ta2S nachgewiesen werden.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19916050122
Permalink