Description / Table of Contents:
Influence of Ga content on the corrosion resistance of NiCr20Mo 10Ga dental alloysThe influence of different gallium contents on the corrosion behavior of Ni-Cr alloys exposed to 0.1 M lactic acid, 0.1 M sodium chloride, 0.005 M potassium thiocyanate has been studied. Five experimental NiCr20Mo 10Ga alloys differing in their gallium contents (0, 5, 7, 10, 15 wt.%) were described by potentiodynamic polarization as well as by analytically determined substance loss measurements. The results revealed that gallium contents up to 10 wt.% improve the corrosion characteristic whereas higher amounts of this very element decrease the corrosion resistance drastically.
Notes:
An fünf experimentellen NiCr20Mo 10Ga Legierungen mit Ga-Gehalten von 0, 5, 7, 10 und 15 Massen-% wurde der Einfluß von Ga auf das Korrosionsverhalten in einer Lösung aus 0,1 M Milchsäure, 0,1 M Natriumchlorid und 0,005 M Kaliumthiocyanat untersucht. Als Untersuchungsmethoden dienten elektrochemische Messungen zur Bestimmung von ECORR, EP, iCORR, RP und analytische Messungen zur Bestimmung der Ionenabgabe. Die Ergebnisse zeigten übereinstimmend, daß die Korrosionsbeständigkeit von NiCr20Mo 10Ga erst ab Ga-Gehalten von über 10 Massen-% verschlechtert wird.
Additional Material:
13 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/maco.19900410805
Permalink