Nanometric ferrihydrite, maghemite and magnetite particles formed within an organicinorganic hybrid matrix were obtained by the sol-gel process. In contrast to precipitation techniques, sol-gel process appears as suitable way to achieve size-controlled nanoscopic magnetic particles anchored in a hybrid structure. The hybrid matrix here reported, named di-ureasil, is composed of poly(oxyethylene) chains grafted to siloxane groups by means of urea cross-linkages. The formation of ferrihydrite particles was achieved incorporating iron nitrate during the sol-gelprocess, at low pH. The formation of maghemite takes place after the incorporation of a mixture of Fe3+ and Fe2+ ions and treatment with an ammonia solution, after the sol-gel process. Magnetite nanoparticles are formed after the incorporation of Fe2+ ions and treatment with ammonia at 80ºC. The AC magnetic susceptibility shows thermal irreversibility with a blocking temperature TB≈13K and ≈25K depending on frequency for the ferrihydrite and maghemite particles, respectively. Themagnetite nanoparticles are blocked at room temperature. Above the irreversibility the magnetization of ferrihydrite and maghemite follows a Langevin function modified with a linear term, as found in antiferromagnetic and ferrimagnetic particles
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/12/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.514-516.142.pdf
Permalink