Description / Table of Contents:
Nitrido-silicates. III [1] High-Temperature Synthesis, Crystal Structure, and Magnetic Properties of Ce3[Si6N11]Pure Ce3[Si6N11] was obtained as transparent yellow crystals by reaction of metallic cerium with silicon diimide (Ce:Si = 1:2) under nitrogen atmosphere in a specially developed high-frequency furnace at 1660°C. Ce3[Si6N11] (P4bm, a = 1013.7(3), c = 483.9(5) pm, Z = 2, R = 0.034, wR = 0.024) contains Ce3+ ions as well as a three-dimensional covalent anionic network structure of corner-sharing SiN4 tetrahedra. Measurements of the magnetic susceptibility gave no indications for magnetic ordering phenomena in the temperature range between 2 and 300 K. Above 100 K pure Curie-Weiss behaviour (μeff = 2,10 μB, determined at room temperature) was observed.
Notes:
Transparent gelbe Kristalle von Ce3[Si6N11] wurden phasenrein durch Umsetzung von metallischem Cer mit Siliciumdiimid (Ce:Si = 1:2) unter Stickstoffatmosphäre in einem speziellen Hochfrequenzofen bei 1660°C synthetisiert. Ce3[Si6N11] (P4bm, a = 1013,7(3), c = 483,9(5) pm, Z = 2, R = 0,034, wR = 0,024) besteht im Festkörper aus Ce3+-Ionen sowie einer kovalenten, dreidimensional vernetzten Anionenteilstruktur eckenverknüpfter SiN4-Tetraeder. Messungen der magnetischen Suszeptibilität ergaben keine Hinweise auf magnetische Ordnungsphänomene im Temperaturbereich von 2 bis 300 K. Oberhalb 100 K wurde reines Curie-Weiss-Verhalten (μeff = 2,10 μB, ermittelt bei Raumtemperatur) beobachtet.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19956210917
Permalink