    Recrystallization of uranium by the action of cyclic heat-treatment (1958)
    Springer
    Atomic energy 4 (1958), S. 729-733 
    Details
    ISSN: 1573-8205
    Quelle: Springer Online Journal Archives 1860-2000
    Thema: Energietechnik , Physik
    Notizen: Abstract During cyclic heat-treatment in the temperature range 100–550 °C with cycles of 50 second duration, recrystallization resulting in a refinement of the original microstructure occurs in uranium quenched from the γ-phase region, as well as in uranium annealed in the γ-phase and in cast uranium, not subjected to additional deformation. Recrystallization commences at places with maximum distortion of the crystal lattice.
    Materialart: Digitale Medien
    URL: http://dx.doi.org/10.1007/BF01515400
    Bibliothek Standort Signatur Band/Heft/Jahr Verfügbarkeit
    BibTip Andere fanden auch interessant ...
    Artikel (Nationallizenzen)
    Volltext
  • 2
    Digitale Medien
    Digitale Medien
    Formation of porosity in uranium under the action of thermal cycling (1957)
    Springer
    Atomic energy 2 (1957), S. 637-643 
    Details
    ISSN: 1573-8205
    Quelle: Springer Online Journal Archives 1860-2000
    Thema: Energietechnik , Physik
    Notizen: Abstract In accelerated thermal cycling with a cycle of 50 sec period, considerable changes appear in uranium after 50–1000 cycles, depending upon the temperature range of the cycle. Cycling in the temperature range of the α-phase (with heating up to between 550 and 600 °C) produces in texturcd uranium (containing about 0.1% carbon) a directional deformation and porosity, accompanied by a drop in density. After 5000 cycles, the drop in density amounts to 8% Thermal cycling with α = ß = γ-transformations produces a pronounced distortion of the original shape of uranium speclmens and intense porosity formation, with a considerable drop in density, which attains 30% after 1000 cycles.
    Materialart: Digitale Medien
    URL: http://dx.doi.org/10.1007/BF01514535
    Bibliothek Standort Signatur Band/Heft/Jahr Verfügbarkeit
    BibTip Andere fanden auch interessant ...
    Artikel (Nationallizenzen)
    Volltext
Schließen ⊗
Diese Webseite nutzt Cookies und das Analyse-Tool Matomo. Weitere Informationen finden Sie hier...