Fatigue properties of a squeeze cast Al-Si-Mg alloy were examined under rotating bendingand the effect of humidity on the crack initiation and propagation behavior was investigated incontrolled humidity. The fatigue strength was decreased in high humidity (RH85%) in comparisonwith the one in low humidity (RH25%). Cracks initiated at the early stage of fatigue life from slipbands and eutectic Si particles in many cases and partially casting defects, and most of fatigue life wasoccupied by the growth life of a small crack regardless of humidity. The propagation of a crack werepromoted by humidity, especially the growth rate of a crack larger than about 100 µm, whichpropagated in tensile mode, was strongly accelerated
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/01/57/transtech_doi~10.4028%252Fwww.scientific.net%252FKEM.385-387.397.pdf
Permalink