Zr and/or Nb added Fe3Al based intermetallic alloys (i.e., Fe3Al-Zr, Fe3Al-Nb andFe3Al-Zr-Nb) were arc-melted, homogenized, hot-rolled and then annealed to evaluate microstructureand tensile property at room temperature as well as at a high temperature (873K). After annealing,the rolled alloys exhibited a recrystallized microstructure containing coarse second phase particles,except for the Nb-added alloy with a minor content of Nb. Relatively high tensile elongation aswell as high tensile strength was observed at room temperature in the Zr-added alloys with a minoramount of Zr. Also, these alloys showed relatively high tensile strength and elongation at high temperature(873K). The results suggest that tensile ductility as well as strength of Fe3Al-based alloyscan be improved by introduction of the second phase dispersions
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/17/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.561-565.395.pdf
Permalink