The effects of helium and aging treatment on radiation damage behavior in low activation Fe-Cr-Mn ( W, V) alloy were investigated by electron and helium ion dual-beam irradiation in a high voltage electron microscope. Specimens were aged at 673 K, 823 K and 923 K for 1000, 3000 and 10000 hours. Electron and He ion dual-beam irradiations were performed at 627 K to 10 dpa. M23C6 type carbides were precipitated in the aged specimens, and the amount of the precipitates was increased with increasing aging temperature and aging time. He bubbles were formed during dual-beam irradiation in all of the specimens. The cavity swelling under dual-beam irradiations was increased with increasing the aging temperature and aging time. It was suggested that cavity swelling is closely related to the concentration of solutes such as Cr and C in the matrix, namely cavity growth rate becomes higher with decreasing of the solutes in solution
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/09/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.475-479.1455.pdf
Permalink