Crack Growth Behaviour of Structural Steels in SeawaterThe influence of a synthetic seawater environment upon the crack growth behaviour of two structural steels was investigated. The results were presented in terms of the stress intensity fracture toughness parameter. Data were generated in air and in seawater with or without a cathodic protection. Results show that seawater environment and a cathodic protection influence the crack propagation at the applied frequencies of 0,04 and 0,25 Hz. The use of cathodic protection raises questions concerning the resistance to hydrogen embrittlement of the two steels. Some fractographic examinations of selected specimens show the microstructure of the two steels at various test conditions.
Notizen:
Die Kenntnis der Ausbreitungsgeschwindigkeit von Rissen an Materialien in korrosiver Atmosphäre unter Betriebsbelastung ist für die Konstruktionsauslegung von großer Bedeutung. Von den Baustählen X70 sowie St70 ist mittels angeschwungener CT-Proben die Rißausbreitung bestimmt worden. Die Versuchsfrequenzen lagen - bezogen auf realistische Seegangsspektren - bei 0,04 Hz und 0,25 Hz. Durch Aufgabe kathodischer Schutzpotentiale wird bei Vorhandensein von Anrissen die Rißausbreitung stark beschleunigt. Es tritt eine wasserstoffinduzierte Spannungsrißkorrosion auf. Über das Ausmaß der Wasserstoffaufname der Bruchflächen werden Angaben gemacht. Durch REM-Aufnahmen wird das Bruchaussehen dokumentiert.
Zusätzliches Material:
15 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/mawe.19810120305
Permalink