The lateral thickness of the polypropylene core crystals in oriented polypropylene (PP)/poly-1-butene (PB-1), blends has been determined by an analysis of the x-ray wide angle scattering. The core crystal thickness decreases with decreasing polypropylene weight fraction from ca. 300 Å (weight average) or 400 Å (number average) to approximately 100 Å. Mixed crystals, where PP and PB-1 chains are solidified, cannot be found. The change of needle thickness with PP-concentration explains the melting point depression that had been measured on the same set of samples. The lattice distortions increase slightly with decreasing PP content. They appear concentrated primarily within a lateral boundary layer, whose thickness is only slightly depended on the core crystal thickness.
Notes:
Die laterale Dicke der Polypropylen-Nadelkristalle in orientierten Blends aus Poly-propylen (PP) und Poly-I-buten (PB-1) wurde durch eine Analyse der Röntgenweitwinkelstreuung bestimmt. Die Nadeldicke nimmt von ca. 300 Å (Gewichtsmittel) bzw. 400 Å (Zahlenmittel) mit abnehmendem Polypropylenanteil auf ca. 100 Å ab. Mischkristalle, in denen sowohl PP- als auch PB-1-Ketten kristallisieren, werden nicht gefunden. Die Änderung der Nadeldicken mit der PP-Konzentration erklärt die an den gleichen Proben gemessene Schmelzpunktsdepression. Die Gitterstörungen nehmen mit abnehmendem PP-Anteil leicht zu. Sie sind im wesentlichen innerhalb einer lateralen Grenzschicht, deren Dicke nur wenig von der Nadeldicke abhängt, konzentriert.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1983.051190101
Permalink