Summary Thermally stimulated currents have been measured in low-density polyethylene in the temperature range from −190 to +40 °C. In this range four peaks are discernable, of which two near −170°C and −135°C are interpreted in terms of electron or hole injection and subsequent detrapping. The depolarisation phenomenon at higher temperatures is strongly sensitive to polarisation temperature and can be explained in terms of dipole orientation.
Notes:
Zusammenfassung Zur Untersuchung des Leitungsmechanismus in Polyäthylen (LDPE) wurden Messungen thermisch stimulierter Ströme im Temperaturbereich von −190 bis +40 °C durchgeführt. Dabei treten, abhängig von der Polarisationstemperatur, bis zu vier, teilweise nur als Schulter ausgeprägte Maxima auf. Zwei Peaks bei tiefer Temperatur, die im wesentlichen unabhängig von der Polarisationstemperatur sind, werden mit Injektion und Trapping von Ladungsträgern (Elektronen oder Löcher) in Verbindung gebracht. Der Hauptpeak bei hoher Temperatur, dessen Erscheinen abhängig von der Polarisationstemperatur ist, kann mit einer Dipolorientierung PE-eigener Dipole erklärt werden.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01498923
Permalink