Keywords:
High-T c superconductor
;
multifilament tape
;
critical bend strain
;
superconducting solenoid
Source:
Springer Online Journal Archives 1860-2000
Topics:
Electrical Engineering, Measurement and Control Technology
,
Physics
Notes:
Abstract Multifilament Ag-sheathed BiPbSrCaCuO (2223) superconducting tapes containing 49 filaments were fabricated by the powder-in-tube route and the roll-anneal process. The transport critical current densityJ c was 1.3×104 A cm−2 at 77 K and 7×104 A cm−2 at 4.2 K in self-field. A 12-m-long tape was used to construct superconducting solenoids (50, 28, and 14 mm internal diameters) generating dc fields 380–1070 G at 4.2 K. Measurements of the variation ofJ c with field (0–1.6 T) and bend strain (0–5%) are used to explain the performance of the solenoids. The critical bend strain of tapes was about 1.5%.