Influence of Lattice Defects of Graphite on the Formation of Graphite HydrogensulfateVarious natural and synthetic graphites were oxidized with chromic acid in sulfuric acid to the 1st stage of graphite hydrogensulfate with the intent of determining the inhibition of intercalation by lattice defects. More oxidant than required by stoichiometry is consumed because slow total oxidation to CO2 is superimposed even at room temperature. The activation energy for total oxidation is reduced by lattice defects. With some graphites, separation of the intercalation reaction from total oxidation was accomplished using calorimetry. The reaction enthalpy in the oxidation of well-crystallized graphites to the graphite salt is -3.05 kJ/mol C.
Notizen:
Die Oxydation verschiedener Natur- und Kunstgraphite mit Chromschwefelsäure zur 1. Stufe des Graphithydrogensulfats wurde untersucht mit dem Ziel, die Hemmung der Intercalation durch Gitterstörungen zu bestimmen. Es wird mehr Oxydationsmittel als stöchiometrisch erforderlich verbraucht, weil auch bei Raumtemperatur langsam Totaloxydation zu CO2 erfolgt. Die Aktivierungsenergie für die Totaloxydation wird durch Gitterstörungen herabgesetzt. Eine Trennung von Intercalationsreaktion und Totaloxydation gelang bei einigen Graphiten durch calorimetrische Messung. Für gut kristallisierte Graphite beträgt die Reaktionsenthalpie für die Oxydation zum Graphitsalz -3,05 kJ/mol.
Zusätzliches Material:
6 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/zaac.19794560113
Permalink