Superconducting films
;
YBa2Cu3O7
;
degradation of superconducting properties
;
critical current density
Quelle:
Springer Online Journal Archives 1860-2000
Thema:
Elektrotechnik, Elektronik, Nachrichtentechnik
,
Physik
Notizen:
Abstract The degradation of epitaxial thin films of YBa2Cu3O7 has been studied as a function of annealing temperature in air and in vacuum; some samples had an evaporated overlayer of CaF2. Degradation was monitored by the measurement of electrical properties after consecutive 30-min annealing treatments. The room-temperature resistance registered significant increases for all samples after annealing at temperatures above about 200°C; the critical current density at 77 K was degraded for annealing temperatures ≥400°C in air, and ≥200–250°C in vacuum. By annealing in oxygen at 550°C, electrical properties were restored in degraded bare YBCO samples annealed in vacuum, but not for those annealed in air.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1007/BF00732247
Permalink