Thin films of cured MY720/DDS epoxy resins were treated with blocking reagents for hydroxyl, amine, and epoxide functional groups. Infrared spectroscopy (IR) and differential scanning calorimetry (DSC) were used to monitor the progress of the reaction. Treated films were soaked in distilled water at 30°C for 720 h, and the corresponding moisture absorption determined gravimetrically. Samples treated with N-methyl-N-t-butyldimethylsilyl trifluroacetamide (MTBSTFA) containing 1% t-butyldimethylchlorosilane (TBDMCS) in dimethylsulfoxide (DMSO) at 30°C showed a maximum reduction in the IR peak at 3400 cm-1 (OH and NH) of 39% and a 100% reduction in the epoxide peak at 904 cm, -1. The moisture absorption was 1.9%, a reduction of 58% compared to the untreated films (ca. 4.5%). The reactions show dependencies on time and temperature and are diffusion controlled. Samples treated with trimethylsilyl isocyanate (TMSI) in DMSO a 70°C showed 72% reduction in the 3400 cm-1 IR peak; DSC thermograms do not show an exothermic energy, suggesting that all epoxide groups reacted. These reactions are primarily dependent on time and temperature. The moisture absorption of TMSI treated samples was 1.0% (75% reduction). Samples were also treated with m-trifluoromethyl phenyliscyanate (MTFPI). The reduction in the IR peak at 3400 cm-1 was 9%, but the moisture absorption was 2.4% - a reduction of 47%.
Zusätzliches Material:
12 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/pol.1985.170231204
Permalink