ISSN:
0736-0266
Schlagwort(e):
Cobalt
;
Chromium
;
Nickel
;
Total knee arthroplasty
;
Total hip arthroplasty
;
Prostheses, porous-coated
;
Life and Medical Sciences
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Medizin
Notizen:
Co, Cr, and Ni concentrations were determined by electrothermal atomic absorption spectrophotometry in serum and urine specimens collected from a group of 28 patients at intervals of from 1 day to 2.5 years after total knee or hip arthroplasty with porous-coated prostheses fabricated of Co-Cr alloy (ASTM F-75-82). Two control groups were also tested: (a) 42 healthy adults and (b) 16 orthopaedic patients after total knee or hip arthroplasty with porous-coated prostheses fabricated predominantly of Ti-Al-V alloy (ASTM F-136-84). All prostheses contained polyethylene components to avoid metal-to-metal contact. Mean Co concentrations in serum and urine were slightly increased in patients with Co-Cr knee implants at 6-120 weeks after surgery, compared with (a) preoperative values, (b) corresponding values in patients with Co-Cr hip implants, and (c) corresponding values in control patients with Ti-Al-V knee and hip prostheses. Substantially increased Co levels were observed in serum and urine of two patients at 7 weeks and 22 months postarthroplasty, associated with loosening of the prostheses; one of the patients also had elevated Cr levels in serum and urine. Although ASTM F-75-82 and F-136-84 alloys contain very little Ni (〈1.0 and 〈0.2% Ni, respectively, by wt), mean Ni concentrations in serum and urine were greatly increased at 1-2 days after implantation of Ti-Al-V and Co-Cr prostheses, diminishing by 2 weeks. The postoperative hypernickelemia and nickeluresis may reflect contamination of the operative field with Ni-containing particles from the drills, cutting jigs, and drilling jigs, or it may represent a previously unrecognized pathophysiological response to surgery.
Zusätzliches Material:
2 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/jor.1100070302
Permalink