Maschinenbau
Beschreibung / Inhaltsverzeichnis:
Behaviour of stainless cast alloys under combined mechanical and corrosive attackIn media with 3000 mg B/1 (as boric acid, H3BO3) and varying chloride contents down to 1 mg Cl-/1 13%-Cr-steels show pitting. Under constant load cracks appear simultaneously. As can be expected, 17%-Cr-steels are more resistant and duplex ferritic austenitic steels exhibit no corrosion cracking in 3% NaCl-solution even after 10 000 hrs. Generally, corrosion resistance improves with increasing contents of ferrite forming elements. Corrosion cracks are interpreted in termes of anodic stress corrosion cracking. Notch impact bending tests with hydrogen charged specimens show that deformability is reduced.
Notizen:
13%-Cr-Stähle zeigen in Lösungen mit 3000 mg B/1 (als Borsäure, H3BO3) und unterschiedlichen Chloridgehalten Lochkorrosion bis herab zu Konzentrationen von 1 mg Cl-/1. Bei mechanischer Zugbeanspruchung treten gleichzeitig Risse auf. 17%-Cr-Stähle sind erwartungsgemäß beständiger und ferritisch-austenitische Stähle zeigen in 3% NaCl-Lösung auch im 10 000 h-Versuch keine Korrosionsrisse. Generell steigt die Beständigkeit mit zunehmendem Anteil an ferritbildenden Elementen. Die Korrosionsrisse werden als anodische Spannungsrißkorrosion interpretiert. Kerbschlagbiegeversuche mit wasserstoffbeladenen Proben ergeben eine Abnahme des Verformungsvermögens.
Zusätzliches Material:
21 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/mawe.19800110707
Permalink