Preparation and Crystal Structure of BaMnS2The compound BaMnS2 can be synthesized by heating an equivalent mixture of BaCO3 and Mn under a current of H2S at 1000°C. The crystal structure was determined by X-ray diffraction techniques. BaMnS2 is orthorhombic, D2h16-Pnma, a = 7.000, b = 4.144, c = 14.00 Å, z = 4. MnS4 tetrahedra linked by corners form waved layers, which are connected by barium ions. BaMnS2 has the same type of structure as the oxide SrZnO2. In the series of tetrahedral structures AxByCz in which A corresponds to an alkali metal or alkaline-earth metal and B to a transition metal, BaMnS2 is the first known example for a sulfide which is isostructural with an oxide.
Notizen:
Durch Umsetzung von BaCO3 mit Mn im H2S-Strom bei 1000°C konnte BaMnS2 rein erhalten werden. Die Kristallstruktur wurde über röntgenographische Untersuchungen an Einkristallen aufgeklärt. Raumgruppe: D2h16-Pnma. Elementarzelle: a = 7,000 Å, b = 4,144 Å, c = 14,00 Å, sie enthält 4 Formeleinheiten. Die Manganatome sind tetraedrisch von Schwefelatomen umgeben. Durch Eckenverknüpfungen der Tetraeder werden gewellte Schichten ausgebildet, die über die Bariumatome zusammengehalten werden. BaMnS2 entspricht in seinem Aufbau dem SrZnO2 und ist damit aus der Reihe der Tetraedergerüststrukturen AxByCz, in denen A für ein Alkali- oder Erdalkalimetall und B für ein Nebengruppenmetall stehen, das erste Beispiel für ein Sulfid, das mit einem Oxid isotyp ist.
Zusätzliches Material:
3 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/zaac.19734020302
Permalink