Dynamic mechanical properties have been investigated for interpenetrating-network systems based on polyol-cured polyurethanes (PU) and 2 to 1 n-butyl acrylate-n-butyl methacrylate (Ac) networks. The systems were formed simultaneously (SIN) from all of the precursors and reactants for both networks in the same vessel, and sequentially (SIPN) by swelling a precured PU with the reactants that will form the Ac network. If the Ac network is formed after gelation of the PU, the IPNs are transparent and appear to have single T (tan δmax) between those of the homonetworks; visible-phase separation occurs if the Ac is intentionally polymerized prior to PU gelation. Damping curves were lower and broader and the T (tan δmax) and rubber moduli were higher for the SIN than for the SIPN systems. Up to 65 percent Ac, the T (tan δmax) data for both SIN and SIPN fit the Gordon-Taylor equation if a T (tan δmax) for the Ac homonetwork 7°C higher than observed is used, suggesting a higher crosslink density for the Ac network under these conditions. The differences in properties of the SIN and SIPN are assumed to be dependent on sample homogeneity and upon the presence of a tin catalyst in the SIN preparation. This can result in limited Ac-network formation and consequent phase separation before PU gelation has occurred, and the catalyst may also increase the extent of interaction, such as grafting or hydrogen-bond formation between the networks.
Zusätzliches Material:
9 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/pen.760250303
Permalink