Schlagwort(e):
polyethylene
;
slow crack growth
;
γ-irradiation
;
crosslinks
;
Physics
;
Polymer and Materials Science
Quelle:
Wiley InterScience Backfile Collection 1832-2000
Thema:
Chemie und Pharmazie
,
Physik
Notizen:
The effects of γ-irradiation were measured in a HDPE and in the resin after it was recrystallized. The fracture mode of the initial material transformed from crazing to complete brittle failure at a critical dose. The failure mode of the recrystallized material transformed from crazing to shear deformation, which produced an extremely long failure time, and finally, at a higher dose, its fracture became brittle. The relationship between morphology and slow crack growth is presented where crosslinking was the major factor. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 1211-1218, 1998