    The Effect of Al Implantation on the Thermal Oxidation of Stainless Steel in Aggressive Environments (2000)
    Springer
    Oxidation of metals 53 (2000), S. 303-323 
    Details
    ISSN: 1573-4889
    Schlagwort(e): ion implantation ; oxidation ; thermal ; stainless steel ; ion-beam analysis ; aluminum
    Quelle: Springer Online Journal Archives 1860-2000
    Thema: Maschinenbau
    Notizen: Abstract AISI-321 steel samples were implanted with Al ions (implantation-energy:40 keV; dose: 2×1017 ions/cm2). Thermal oxidationof the samples was performed at 450, 550, 600, and 650°C for periodsvarying from 1 to 6 days in air and in a corrosive CO2-containingenvironment. Nuclear Reaction Analysis (NRA) and Rutherford BackscatteringSpectrometry (RBS) were used to investigate the oxidized samples. Asignificant improvement of the oxidation resistance of the implantedmaterial in comparison to the nonimplanted material was observed. Thisespecially applies for samples oxidized at high temperatures. The aluminumdepth distribution determined by NRA [using the resonance at 992 keV of the27Al(p, γ )28Si nuclear reaction] and RBS,indicated no variation of the Al profile in the temperature region450–600°C, whereas at 650°C a slight Al diffusion wasobserved. Scanning electron microscopy (SEM–EDS) was applied to studythe surface morphology and the constitution of the oxide scale formed, aswell as to explain the influence of Al implantation on the oxidation behaviorof AISI-321 austenitic stainless steel.
    Materialart: Digitale Medien
    URL: http://dx.doi.org/10.1023/A:1004541220830
    Bibliothek Standort Signatur Band/Heft/Jahr Verfügbarkeit
    BibTip Andere fanden auch interessant ...
    Artikel (Nationallizenzen)
    Volltext
Schließen ⊗
Diese Webseite nutzt Cookies und das Analyse-Tool Matomo. Weitere Informationen finden Sie hier...