Dy-α-sialon and β-Si3N4 materials containing Dy-oxynitride glass were hot pressed at 1800°C for 1 h. The luminescence spectra of Dy3+ in these samples were compared when excited at 350 nm. The results showed that two strong emission bands in the region 470–500 nm and 570-600 nm, associated with the 4F9/2→6H15/2 and 4F9/2→6H13/2 transitions of Dy3+ ions, were observed in Dy-α-sialon. However, no emission peak was detected from the β-Si3N4 sample, despite it containing the same amount of Dy3+ cations. This proved that only the Dy3+ cations in the α-sialon structure, not those in the oxynitride glass, produce the luminescence spectrum.