Abstract
At anisothermic thermograms registered when curing the urea/formaldehyde (UF) resins in high pressure DSC cell the endothermic effects, such as evaporation of water and elimination of formaldehyde shift to temperatures higher by about 40°C in comparison to the thermograms received using the cell without pressure. The temperature for the exotherma of curing remains unchanged. Due to the shift of decomposition temperature the elimination of formaldehyde takes place at more agreeable conditions: as the resin is more rigid the risk of additional endothermic effect connected with bubble blowing is diminished. The shift of water elimination temperature however disturbs at clear recognition of the base line of the endotherma. Preliminary treating of samples with inert gas before the measurements helps to improve the measurement conditions.
Zusammenfassung
Das thermische Verhalten beim Aushärten von UF-Harzen wurde unter hohem Druck in DSC-Meßzellen verfolgt. Es zeigte sich, daß die endothermen Effekte (Verdampfen von Wasser, Abgabe von Formaldehyd) unter Druck bei um 40°C höheren Temperature erfolgen. Dagegen bleibt der Temperaturbereich der exothermen Reaktionen unverändert. Aufgrund dieser Verschiebung erfolgt die Abgabe von Formaldehyd unter günstigeren Bedingungen als ohne Druck: das Harz ist in diesem Zustand fester und das Risiko zusätzlicher endothermer Effekte (z. B. Platzen von Dampfblasen) ist geringer. Dagegen wirkt sich die höhere Temperaturs der Wasserabspaltung störend aus für das eindeutige Erkennen der Basislinie. Eine vorangehende Behandlung mit Inertgasen verbessert die Versuchsbedingungen.
Similar content being viewed by others
Literatur
M. Szesztay, Zs. László-Hedvig, E. Kovacsovics, F. Tüdös: DSC application for characterization of Urea/formaldehyde condensates, Holtz Roh-Werkstoff, 51 (1993): 297–300
M. Szesztay, Zs. László-Hedvig, C. Takács, E. Gács-Baitz, P. Nagy, F. Tüdös: pH Control of the condensation reaction and its effect on the properties of formaldehyde/urea resins Angew. Makromol., Chem., 215 (1994): 79–91
Author information
Authors and Affiliations
Additional information
The authors express their gratitude to Mrs Ilona Szigeti for her assistance in experimental work and to the National Research Foundation (OTKA) for their financial support
Rights and permissions
About this article
Cite this article
Szesztay, M., László-Hedvig, Z., Nagy, P. et al. DSC characterisation of urea/formaldehyde condensates, II. Experiences with high pressure DSC cell. Holz als Roh- und Werkstoff 54, 399–402 (1996). https://doi.org/10.1007/s001070050209
Issue Date:
DOI: https://doi.org/10.1007/s001070050209