Highly monodisperse polystyrene microparticles cross-linked with urethane acrylates were produced by dispersion polymerization in ethanol solution in the presence of 2,2′-azobis (isobutyronitrile) initiator, polyvinylpyrrolidone stabilizer, and Aerosol–OT costabilizer. Different from conventional crosslinkers, the urethane acrylates employed as a crosslinker showed an excellent effect on maintaining the monodispersity of polystyrene microparticles even in the moderate crosslinker concentration. This was believed that the urethane acrylate helped forming the monomer-swellable surface of primary particles, because of its structurally long tetramethylene oxide groups in its molecule. However, at high concentration of the urethane acrylate, the rough surface and the coagulum of particles were observed, which was attributed to the seriously decreased solubility of the monomer mixtures in ethanol solution. The solubility of the mixtures of styrene monomer and urethane acrylate in the media had a serious effect on the average particle size and morphology of the final particles. This could be confirmed by the measurement of cloud points and fractional conversions.
Similar content being viewed by others
Author information
Authors and Affiliations
Additional information
Received: 21 February 1997 Accepted: 25 May 1998
Rights and permissions
About this article
Cite this article
Kim, JW., Suh, KD. Highly monodisperse crosslinked polystyrene microparticles by dispersion polymerization. Colloid Polym Sci 276, 870–878 (1998). https://doi.org/10.1007/s003960050323
Issue Date:
DOI: https://doi.org/10.1007/s003960050323