Abstract
The hyperfine interactions at In and Sn sites of In2O3∶Sn (ITO) were measured through time-differential perturbed angular correlations and Mössbauer spectroscopy, respectively. Polycrystalline samples prepared by co-precipitation with nominal 0.025, 1 and 5 at.% Sn were studied. They all showed the cubic bixbyite structure characteristic of In2O3 after annealings at 200 °C. The quadrupole interaction at In sites appears nearly independent of Sn concentration being the main result of the presence of Sn in the lattice, the gradual disappearence of the dynamic perturbation caused by after-effects. The Mössbauer data demonstrate that Sn ions are in a 4+ state with ΔQ=0.606 mm/s andδ=0.226 mm/s relative to SnO3Ca at room temperature.
Similar content being viewed by others
References
Z.M. Jarzebski, Phys. Stat. Sol. (a) 71(1982)13.
H. Köstlin, R. Jost and W. Lems, Phys. Stat. Sol. (a) 29(1975)87.
J. Desimoni, A.G. Bibiloni, L.A. Mendoza-Zélis, A.F. Pasquevich, F.H. Sánchez and A.R. López-García, Phys. Rev. B28(1983)5739;
A.G. Bibiloni, J. Desimoni, C.P. Massolo, L.A. Mendoza-Zélis, A.F. Pasquevich, F.H. Sánchez and A.R. López-García, Phys. Rev. B29(1984)1109.
G. Frank, R. Olazcuaga and A. Rabenau, Inorg. Chem. 16(1977)1251.
A.F. Pasquevich, F.H. Sánchez, A.G. Bibiloni, J. Desimoni and A.R. López-García, Phys. Rev. B27(1983)963.
A.G. Bibiloni, C.P. Massolo, J. Desimoni, L.A. Mendoza-Zélis, F.H. Sánchez, A.F. Pasquevich, L. Damonte and A.R. López-García, Phys. Rev. B (to be published).
M. Marezio, Acta Cryst. 20(1966)723.
B.K. Vainshtein, in:Modern Crystallography I, Springer Series in Solid State Sciences, Vol. 15, ed. H.J. Queiser (Springer Verlag, Berlin, 1981) p. 238.
J.C.C. Fan and J.B. Goodenough, J. Appl. Phys. 48(1977)3524.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mercader, R.C., Sánchez, F.H., Mendoza-Zélis, L.A. et al. Hyperfine characterization of tin-doped indium sesquioxide. Hyperfine Interact 23, 211–220 (1985). https://doi.org/10.1007/BF02058077
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02058077