A series of experiments are described which identify those characteristics of charcoals which are important for gunpowder manufacture. Charcoals from Alder Buckthorn, Alder, Beech and Douglas Fir woods were prepared by carbonization under nitrogen in the heat-treatment temperature range 523 to 1173 K. The charcoals were characterized by elemental analysis, differential thermal analysis, measurement of spontaneous ignition temperature, morphology using scanning electron microscopy, surface-area assessment using carbon dioxide as adsorbate, mercury porosimetry and microstrength analyses. Results indicate that for charcoals with acceptable carbon contents of 70 to 80 wt %, extremely fine control of carbonization conditions is required. The surface area and carbon content of the charcoal increased rapidly on heat treatment. The surface area of the charcoal reached values of −400 m2 g−1. Mercury porosimetry indicated that Alder Buckthorn and Douglas Fir charcoals had cumulative pore volumes greater than Alder charcoal and substantially greater than Beech charcoal. The Beech charcoal was the most friable of the three hardwood charcoals tested using microstrength analysis. Alder Buckthorn and Alder charcoals are recommended for gunpowder manufacture.
Similar content being viewed by others
References
J. Robertson, MOD (PE) Unpublished report (1983).
J. D. Blackwood andF. P. Bowden,Proc. Roy. Soc. A213 (1952) 285.
A. Douillet,Memorial des Poudres 37 (1955) 167.
C. Campbell andG. Weingarten,Trans. Faraday Soc. 55 (1959) 222.
K. J. White andR. A. Sasse, Memorandum Report, ARBRL-MR-03219, US Army Armament R and D Command, US Army Ballistic Research Laboratory, Aberdeen Proving Ground, Maryland (1982).
T. Urbanski, W. Hofman, R. Ostrowski andM. Witanowski,Bull-Acad. Polon. Sci. Ser. Sci. Chim. Geol. et Geograph. 7 (1959) 851.
Idem, ibid. 7 (1959) 861.
T. Urbanski,Explosivstoffe (1968) 200.
W. Hintze,ibid. (1968) 41.
H. L. Porter andJ. C. Stimson, ARE Memo 5/52 (1952).
A. D. Kirshenbaum,Thermochim. Acta 18 (1978) 113.
Anonymous “Charcoal Wood for Explosives and Pyrotechnics” DEF-STAN, 91-31 (1977).
F. Baddeley, Pamphlet on the Manufacture of Gunpowder as Carried on at the Government Factory, Waltham Abbey (HMSO, 1857).
F. M. Smith, “A Handbook of the Manufacture and Proof of Gunpowder” (Waltham Abbey, HMSO, 1870).
Anonymous Proceedings of the Ordnance Board, No. 36, 670 (1951).
E. Gray, H. Marsh andM. McLaren,J. Mater. Sci. 17 (1982) 3385.
P. H. Emmett andS. Brunauer,J. Amer. Chem. Soc. 59 (1937) 1553.
J. A. Baker andE. J. Poziomek,Carbon 12 (1974) 45.
H. L. Riley,Gas World, Coking Section 25 (1937) 118.
W. E. Hillis, “Wood Extractives and Their Significance to the Pulp and Paper Industries” (Academic Press, New York, 1962).
A. J. Panshin andC. deZeeuw, “Textbook of Wood Technology”, 4th Ed. (McGraw Hill, New York, 1980).
T. E. Timell,Adv. Carbohydrate Chem. 20 (1965) 409.
K. V. Sarkanen andC. H. Ludwig (Eds), “Lignins” (Interscience, New York 1971).
B. Grimshaw andR. Perry, MOD, unpublished results (1980).
Forest Products Research Bulletin No. 46 (HMSO, London, 1961).
F. H. Schweingruber, “Microscopic Wood Anatomy”, Swiss Federal Institute of Forestry Research, Birmensdorf (1978).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Gray, E., Marsh, H. & Robertson, J. Physical characteristics of charcoal for use in gunpowder. J Mater Sci 20, 597–611 (1985). https://doi.org/10.1007/BF01026531
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01026531