Summary
Perpendicular magnetic-field transitions of pure Sn films, assessed by microwave absorption measurement as a function of specimen thickness (65 nm÷200 μm) and temperature (1.5 K÷T c), are presented. The passage from intermediate- to mixed-state behaviour was observed. The values obtained for the critical thickness d ⊥ at which the passage from type-I to type-II behaviour occurs agree with theoretical predictions. Critical perpendicular magnetic-field values, H ⊥, also agree well with theoretical predictions for d<d ⊥ and in the limit d≫d ⊥.
Riassunto
In questo lavoro si studia, con una tecnica differenziale a microonde, la transizione superconduttiva di film di stagno in campo magnetico perpendicolare. Le misure sono state effettuate in funzione dello spessore (65 nm÷200 μm) e della temperatura (1.5 K÷T c). È stato osservato il passaggio fra lo stato intermedio e lo stato misto e sono stati determinati i valori dello spessore critico, d ⊥, a cui avviene tale passaggio; i valori ottenuti sono in accordo con le previsioni teoriche. Inoltre l'andamento del campo magnetico critico perpendicolare, H ⊥, in funzione dello spessore è in buon accordo con le previsioni teoriche per d<d ⊥ e nel limite d≪d ⊥.
Резюме
С помощью измерений микроволнового поглощения исследуются переходы, связанные с перпендикулярным магнитным полем, для пленок чистого олова, как функция толщины образцов (65 нм÷200 мкм) и температуры (1.5 K÷T c). Наблядается переход от промежуточного к смешанному состоянию. Значения, полученные для критической толщины d ⊥, при которой имеет место переход от поведения типа I к поведению типа II, согласуется с теоретическими предсказаниями. Критические значения перпендикулярного магнитного поля H ⊥ также согласуются с теоретическими предсказаниями для d<d ⊥ и в пределе d≫d ⊥.
Similar content being viewed by others
References
E. Di Crescenzo, M. Flamini, P. L. Indovina, S. Onori and A. Rosati: Ann. Ist. Sup. San., 7, 560 (1971).
E. Di Crescenzo, P. L. Indovina, S. Onori and A. Rogani: Phys. Rev. B, 7, 3058 (1973).
P. L. Indovina, S. Onori, A. Rogani, E. Tabet and P. Tonna: Solid State Commun., 20, 85 (1976).
R. E. Miller and G. D. Cody: Phys. Rev., 173, 494 (1968).
B. L. Brandt, R. D. Park and R. D. Chaudhari: J. Low Temp. Phys., 4, 41 (1971).
M. D. Maloney, F. de la Cruz and M. Cardona: Phys. Rev. B, 5, 3558 (1972).
G. J. Dolan and J. Silcox: Phys. Rev. Lett., 30, 603 (1973).
T. Miyazaki, B. Shinozaki, R. Aoki, M. Katayama and S. Yamashita: J. Phys. Soc. Jpn., 45, 1487 (1978).
M. Tinhkam: Phys. Rev., 129, 2413 (1963).
G. Lasher: Phys. Rev., 154, 345 (1966).
G. Maki: Ann. Phys. (N. Y.), 34, 363 (1965).
P. B. Ayscough: Electron Spin Resonance in Chemistry (London, 1967), p. 149.
R. J. Pedersen, Y. B. Kim and R. S. Thompson: Phys. Rev. B, 7, 982 (1973).
J. I. Gittleman, S. Bozowski and B. Rosemblum: Phys. Rev., 161, 398 (1967).
P. G. de Gennes and D. Saint-James: Phys. Lett., 7, 306 (1963).
Yu. V. Sharvin: Sov. Phys. JETP, 6, 1031 (1958).
T. E. Faber: Proc. R. Soc. London, Ser. A, 248, 460 (1958).
E. A. Davies: Proc. R. Soc. London, Ser A, 255, 407 (1960).
S. Onori and A. Rogani: Physica B, 100, 93 (1980).
E. Guyon, C. Caroli and A. Martinet: J. Phys. (Paris), 25, 683 (1964).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Flamini, M., Onori, S. & Rogani, A. Microwave study of intermediate- to mixed-state behaviour changes in tin superconducting films. Il Nuovo Cimento D 2, 1497–1508 (1983). https://doi.org/10.1007/BF02460228
Received:
Revised:
Issue Date:
DOI: https://doi.org/10.1007/BF02460228